This material is frosted clear after post-cure. It offers high impact strength and scratch resistance. It has good mechanical properties and high dimensional accuracy.
It is mainly used in Flow Analysis, Architecture, Lightning Applications and Art.
Material Data:
Characteristic | Method | Symbol | R060 |
---|---|---|---|
Clear | |||
Applications | Fluid/Flow analysis, Architecture, Art | ||
Physical Properties | |||
Hardness Shore D | DIN EN ISO 48-4 | D | 85,6 |
Solid Density | DIN EN ISO 1183-1 | ρ | 1.19 g/cm³ |
Tensile properties | |||
Tensile Modulus | ASTM D638, Type I | Et | 2258 MPa |
Tensile Strength | ASTM D638, Type I | σM | 46.7 MPa |
Elongation at Tensile Strength | ASTM D638, Type I | εM | 3,93 % |
Elongation at Break | ASTM D638, Type I | εtB | 4,14 % |
Bending properties | |||
Flexural Modulus | ASTM D790 | Ef | 1991 MPa |
Flexural Strength | ASTM D790 | σfM | 64.9 MPa |
Deflection at Flexural Strength | ASTM D790 | εfM | 4,96 % |
Deflection at Break | ASTM D790 | εfB | > 5.0 % |
Impact Strength Properties | |||
IZOD Notched | ASTM D256 | aiN | 2.63 KJ/m² (26.6 J/m) |
Thermal Properties | |||
HDT @ 0.45 N/mm² | ASTM D 648 (B) | Tf | 53.5 °C |
Glow wire flammability index | DIN EN 60695-2-12 | GWFI | - |
Glass Transition Temperature | DIN EN ISO 11359 | Tg | - |
Linear Expansion Coeff. -20°C … 20°C | DIN EN ISO 11359 | α | - |
Linear Expansion Coeff. 65°C … 80°C | DIN EN ISO 11359 | α | - |
Curl / Vertical Distortion | |||
Dimensional Accuracy XY | Test Print (100x100x6mm) | 99,65% | |
Curl on Test bar (200x20x5mm) | Vertical Print Orientation | 0mm | |
Curl on Cantilever Test bar (200x20x5mm) | Horizontal Print Orientation | 0.1 mm | |
Printing Speed | |||
Print Speed (cm³/hour) | 2150 | ||
Conditions: Printed on Solidator V3, Layer Height 100 micron, Cleaned in Isopropanol < 3 min, Air Brush Clean, Post Cure with Solidator Cure Box | |||