The resin in white color is especially suitable for architectural models.
It offers high impact strength, low warpage and high dimensional stability. This also allows the use as functional components.
Material Data:
| Characteristic | Method | Symbol | R051 |
|---|---|---|---|
| White | |||
| Applications | Models, Architecture, Art | ||
| Physical Properties | |||
| Hardness Shore D | DIN EN ISO 48-4 | D | 80,2 |
| Solid Density | DIN EN ISO 1183-1 | ρ | 1.21 g/cm³ |
| Tensile properties | |||
| Tensile Modulus | ASTM D638, Type I | Et | - |
| Tensile Strength | ASTM D638, Type I | σM | 33.0 MPa |
| Elongation at Tensile Strength | ASTM D638, Type I | εM | - |
| Elongation at Break | ASTM D638, Type I | εtB | - |
| Bending properties | |||
| Flexural Modulus | ASTM D790 | Ef | - |
| Flexural Strength | ASTM D790 | σfM | - |
| Deflection at Flexural Strength | ASTM D790 | εfM | - |
| Deflection at Break | ASTM D790 | εfB | >5% |
| Impact Strength Properties | |||
| IZOD Notched | ASTM D256 | aiN | - |
| Thermal Properties | |||
| HDT @ 0.45 N/mm² | ASTM D 648 (B) | Tf | - |
| Glow wire flammability index | DIN EN 60695-2-12 | GWFI | - |
| Glass Transition Temperature | DIN EN ISO 11359 | Tg | - |
| Linear Expansion Coeff. -20°C … 20°C | DIN EN ISO 11359 | α | - |
| Linear Expansion Coeff. 65°C … 80°C | DIN EN ISO 11359 | α | - |
| Curl / Vertical Distortion | |||
| Dimensional Accuracy XY | Test Print (100x100x6mm) | 99,71% | |
| Curl on Test bar (200x20x5mm) | Vertical Print Orientation | 0mm | |
| Curl on Cantilever Test bar (200x20x5mm) | Horizontal Print Orientation | 0.05 mm | |
| Printing Speed | |||
| Print Speed (cm³/hour) | 1702 | ||
| Conditions: Printed on Solidator V3, Layer Height 100 micron, Cleaned in Isopropanol < 3 min, Air Brush Clean, Post Cure with Solidator Cure Box | |||