Solidator Black Resin (R010)

Solidator Black Resin offers medium strength and medium bend-resistance. It is particularly suitable for initial design iterations, figures and housing parts used under ambient temperature and medium load or impact conditions. Since June 2017, this material has been used to produce parts for the Solidator 3D printer.


3d printed prototyps

Material Data:

Characteristic Method Symbol R010
Black
Applications Electronic Housings, Figures, Connectors, Brackets
Physical Properties   
Hardness Shore D DIN EN ISO 48-4 D 84,6
Solid Density DIN EN ISO 1183-1 ρ 1.19 g/cm³
Tensile properties   
Tensile Modulus ASTM D638, Type I Et 1910 MPa
Tensile Strength ASTM D638, Type I σM 36.6 MPa
Elongation at Tensile Strength ASTM D638, Type I εM 3,11 %
Elongation at Break ASTM D638, Type I εtB 3,20 %
Bending properties   
Flexural Modulus ASTM D790 Ef 2122 MPa
Flexural Strength ASTM D790 σfM 64.1 MPa
Deflection at Flexural Strength ASTM D790 εfM 4,69 %
Deflection at Break ASTM D790 εfB > 4.24%
Impact Strength Properties   
IZOD Notched ASTM D256 aiN 1.29 kJ/m² (13.1 J/m)
Thermal Properties   
HDT @ 0.45 N/mm² ASTM D 648 (B) Tf 53.3 °C
Glow wire flammability index DIN EN 60695-2-12 GWFI 650 °C / 3.1 mm
Glass Transition Temperature DIN EN ISO 11359 Tg 22
Linear Expansion Coeff.  -20°C … 20°C DIN EN ISO 11359 α 94 * 10-6 K-1
Linear Expansion Coeff.  65°C … 80°C DIN EN ISO 11359 α 195 * 10-6 K-1
Curl / Vertical Distortion   
Dimensional Accuracy XY Test Print (100x100x6mm) 99,56%
Curl on Test bar (200x20x5mm) Vertical Print Orientation 0mm
Curl on Cantilever Test bar (200x20x5mm) Horizontal Print Orientation 1.0 mm
Printing Speed   
Print Speed (cm³/hour) 2213
Conditions: Printed on Solidator V3, Layer Height 100 micron, Cleaned in Isopropanol < 3 min, Air Brush Clean, Post Cure with Solidator Cure Box