The resin “Solidator Professional Translucent Orange” has high scratch-resistance, high bending resistance good tensile strength and high heat deflection temperature.
Ideal for mold-making and prototyping of small to medium sized objects.
Material Data:
| Characteristic | Method | Symbol | R001 |
|---|---|---|---|
| Translucent Orange | |||
| Applications | Prototyping, Molds | ||
| Physical Properties | |||
| Hardness Shore D | DIN EN ISO 48-4 | D | 84,7 |
| Solid Density | DIN EN ISO 1183-1 | ρ | 1.18 g/cm³ |
| Tensile properties | |||
| Tensile Modulus | ASTM D638, Type I | Et | 2101 MPa |
| Tensile Strength | ASTM D638, Type I | σM | 40.7 MPa |
| Elongation at Tensile Strength | ASTM D638, Type I | εM | 3,45 % |
| Elongation at Break | ASTM D638, Type I | εtB | 3,54 % |
| Bending properties | |||
| Flexural Modulus | ASTM D790 | Ef | 2735 MPa |
| Flexural Strength | ASTM D790 | σfM | 99.3 MPa |
| Deflection at Flexural Strength | ASTM D790 | εfM | 4,90 % |
| Deflection at Break | ASTM D790 | εfB | > 5.0 % |
| Impact Strength Properties | |||
| IZOD Notched | ASTM D256 | aiN | 1.58 kJ/m²/(16 J/m) |
| Thermal Properties | |||
| HDT @ 0.45 N/mm² | ASTM D 648 (B) | Tf | 66.3 °C |
| Glow wire flammability index | DIN EN 60695-2-12 | GWFI | 625 °C / 2.9 mm |
| Glass Transition Temperature | DIN EN ISO 11359 | Tg | 49 |
| Linear Expansion Coeff. -20°C … 20°C | DIN EN ISO 11359 | α | 92 * 10-6 K-1 |
| Linear Expansion Coeff. 65°C … 80°C | DIN EN ISO 11359 | α | 205 * 10-6 K-1 |
| Curl / Vertical Distortion | |||
| Dimensional Accuracy XY | Test Print (100x100x6mm) | 99,81% | |
| Curl on Test bar (200x20x5mm) | Vertical Print Orientation | 0mm | |
| Curl on Cantilever Test bar (200x20x5mm) | Horizontal Print Orientation | 1.0 mm | |
| Printing Speed | |||
| Print Speed (cm³/hour) | 1897 | ||
| Conditions: Printed on Solidator V3, Layer Height 100 micron, Cleaned in Isopropanol < 3 min, Air Brush Clean, Post Cure with Solidator Cure Box | |||